EFFECT OF Li+ CO-DOPING ON THE LUMINESCENCE PROPERTIES OF ZnO:Tb3+ NANOPHOSPHORS
Аннотация:
Li+ co-doped ZnO:Tb3+ nanocrystals were synthesized via the chemical co-precipitation method in order to study the effect of Li+ co-doping. The samples were characterized by means of SEM, XRD, FTIR, Reflectance, PL and TL studies. SEM images showed that the samples were composed of nanorods with diameters of 50 to 90 nm and lengths of approximately 600 nm to 1.3µm. XRD analysis revealed pure phase of ZnO with hexagonal wurtzite structure. XRD study also showed no change in the peak pattern for Li+ co-doping; a slight shift of the (101) peaks towards lower angle can be seen. Sample crystal sizes were found to be in the 10–25 nm range. Photoluminescence intensity was enhanced due to a minute amount of Li+ co-doping in the sample. The X-induced thermoluminescence gave a glow peak at 320 ˚ C for the Li+ co-doped sample, which was shifted to a lower temperature and had twice the intensity of the ZnO:Tb3+ sample.
Ключевые слова:
Постоянный URL
Статьи в номере
- METHOD OF SYMMETRIC POLYNOMIALS IN THE COMPUTATIONS OF SCATTERING MATRIX
- HEAT TRANSPORT IN MARANGONI LAYERS WITH NANOPARTICLES
- MODEL OF NON-AXISYMMETRIC FLOW IN NANOTUBE
- ABSORPTION OF ELECTROMAGNETIC RADIATION IN THE QUANTUM WELL PLACED IN A MAGNETIC FIELD
- ULTRASHORT OPTICAL PULSE PROPAGATION IN A DOUBLE LAYER OF GRAPHENE BORON NITRIDE WITH ACCOUNTING THE MATERIAL DISPERSION
- INTERATOMIC INTERACTION IN FCC METALS
- PRE-CHROMATOGRAPHY CRUDE SEPARATION OF LIGHT FULLERENES BY POLY-TERMICAL (RE)CRYSTALLIZATION METHOD
- STRUCTURE PECULIARITIES OF NANOCRYSTALLINE SOLID SOLUTIONS IN GdAlO3 — GdFeO3 SYSTEM
- DIELECTRIC STUDIES OF NANOCRYSTALLINE MANGANESE TUNGSTATE
- STRUCTURAL PROPERTIES OF COBALT SUBSTITUTED BARIUM HEXAFERRITE NANOPARTICLES PREPARED BY A THERMAL TREATMENT METHOD
- PREPARATION AND ANTIMICROBIAL OBSERVATIONS OF ZINC DOPED NANOHYDROXYAPATITE
- DIELECTRIC WAVEGUIDE OPTIMIZATION FOR THE ENHANCEMENT OF TE-POLARIZATION TRANSMISSION OF PLASMONICS-BASED MSM-PD
- SILVER-NANOPARTICLE-BASED ETCH MASK CONTROL FOR SUBWAVELENGTH STRUCTURE DEVELOPMENT
- THE EFFECTS OF DEFECTS ON ELECTRON TRANSPORT IN METALLIC SINGLE WALL CARBON NANOTUBES
- ELECTROFABRICATION OF NANOSTRUCTURED MULTILAYER COATINGS FOR BETTER CORROSION PROTECTION
- NOISE CANCELLATION IN UNSHIELDED MAGNETOCARDIOGRAPHY BASED ON LEAST-MEAN-SQUARED ALGORITHM AND GENETIC ALGORITHM
- COMPOSITES OF SINGLE WALLED CARBON NANOTUBES AND LIQUID CRYSTALS AS SWITCHABLE CONDUCTORS
- EFFECT OF SINTERING TEMPERATURE ON THE STRUCTURAL AND MAGNETIC PROPERTIES OF COBALT FERRITE NANOPARTICLES